Methylated N-methylol melamine (NMM) is known for its ability to enhance physico-mechanical properties, anti-fungal ability, and hydrophobicity and was therefore used to impregnate two less used and non-durable wood species from Myanmar, Bombax ceiba and Bombax insigne. Solution uptake, weight percent gain and nitrogen content were increased by increasing melamine concentrations with B. ceiba always achieving higher values compared with B. insigne. According to the leaching results, a higher degree of condensation after curing as well as a better crosslinking of NMM could be obtained at higher temperatures. However, both curing temperatures used (90 and 120 °C) resulted in almost the same amount of nitrogen fixed in the cell wall. UV microspectrophotometry confirmed the penetration of the NMM into different morphological regions of wood tissues, which was again supported by the analysis of point measurement spectra of treated and untreated specimens.